دانشگاه سمنان شیمى کاربردى روز 2981-2437 1396 ویژه نامه دومین سمینار شیمی کاربردی ایران، شهریور 1396 2018 12 22 Application of an effective self-healing coating on copper surface استفاده از پوشش خود ترمیم موثر بر روی فلز مس 72 81 3543 10.22075/chem.2018.3543 FA Journal Article 2019 01 06 <em>The self-healing coating consisting of healing and anti-corrosion agents was prepared and its performance on the copper films</em><em>was investigated. The fourier-transform infrared spectroscopy (FTIR) and field emission scanning electron microscopy (FESEM) techniques were applied for chemical structure and surface morphology investigations respectively. The anti-corrosion effect and self-healing process of the coatings was studied by electrochemical impedance spectroscopy (EIS) and FESEM respectively. Taguchi method was used to design the experiments and anti-corrosion efficiency evaluations. The diameter of synthesized nanocapsules was about 459–712 nm. The obtained loading efficiency was about 60%. Coatings containing self-healing and anti-corrosion agents together showed the best result. </em> <em>عملکرد پوششهای خودترمیم شونده­ی هیبریدی اپوکسی و پلی یورتانی حاوی نانوکپسولهای بارگذاری شده با روغن بزرک و پتاسیم اتیل زانتات و بنزوتری آزول بر روی فیلمهای مسی مورد بررسی قرار گرفت. بدین ترتیب که ویژگی های نانوکپسولهای سنتز شده با استفاده از تکنیکهایی مانند </em><em>FTIR</em><em> و </em><em>SEM</em><em> (به ترتیب برای بررسی ساختار شیمایی و مورفولوژی نانوکپسولها) مطالعه شد. خاصیت ضد خوردگی پوششهای تهیه شده با استفاده از تکنیکهای </em><em>EIS</em><em> مورد بررسی قرار گرفت. سطح نمونه­ها و فرآیند خود ترمیمی توسط </em><em>FESEM</em><em> مورد بررسی قرار گرفت. جهت کاهش تعداد آزمایشهای طراحی شده و همچنین بررسی  عملکرد پوششها از روش تاگوچی بهره برده شد.</em> https://chemistry.semnan.ac.ir/article_3543_a38bb232e0ee2838470340cfb24c14c2.pdf